Register of building materials used for this application, cross-section
(from outside to inside)
|
Thickness [mm] |
Building material |
Thermal performance |
Reaction to fireklasse EN |
| λ |
μ min – max |
ρ |
c |
| A |
24,0
|
larch wood
external wall cladding
|
0,155
|
150
|
600
|
1,600
|
D
|
| B |
30,0
|
spruce wood
battens offset (30/50; 30/80) - ventilation
|
0,120
|
50
|
450
|
1,600
|
D
|
| C |
|
wind barrier
|
|
|
1000
|
|
|
| D |
16,0
|
particleboard
|
0,130
|
50-100
|
700
|
1,700
|
D
|
| E |
|
construction timber
(60/..; e=*)
|
0,120
|
50
|
450
|
1,600
|
D
|
| F |
|
- variable insulation material
|
|
|
|
|
|
| G |
16,0
|
particleboard
|
0,130
|
50-100
|
700
|
1,700
|
D
|
| H |
|
vapour barrier sd≥ 5m
|
|
|
1000
|
|
|
| I |
12,5
|
gypsum plaster board type DF
or
|
0,250
|
10
|
800
|
1,050
|
A2
|
| I |
12,5
|
gypsum fibre board
|
0,320
|
21
|
1000
|
1,100
|
A2
|
Variations of building components
|
Thickness of layer |
Note |
Fire performance |
Thermal performance |
Acoustic performance |
Eco Sustainability |
Mass |
|
Thickness [mm] |
Building material |
Σ |
REI |
U [W/(m²K)] |
Diffusion |
Rw (C,Ctr) [dB] |
ΔOI3 |
m [kg/m²] |
|
awrhho02a-00
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
258,5
|
e=625
|
60
from inside
30
from outside
|
0,26
|
adequate
|
47
(-2,-8)
|
24,83
|
37,1
|
|
awrhho02a-01
|
E
F
|
120,0
120,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
218,5
|
e=625
|
60
from inside
30
from outside
|
0,33
|
adequate
|
46
(-2,-8)
|
22,16
|
34,6
|
|
awrhho02a-02
|
E
F
|
200,0
200,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
298,5
|
e=625
|
60
from inside
30
from outside
|
0,22
|
adequate
|
48
(-2,-8)
|
27,45
|
39,6
|
|
awrhho02a-03
|
E
F
|
240,0
240,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
338,5
|
e=625
|
60
from inside
30
from outside
|
0,18
|
adequate
|
49
(-2,-8)
|
30,10
|
42,1
|
|
awrhho02a-04
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [035; 50; <1000°C]
|
258,5
|
e=625
|
60
from inside
30
from outside
|
0,24
|
adequate
|
48
(-2,-8)
|
42,99
|
42,0
|
|
awrhho02a-05
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [038; ≥33; ≥1000°C]
|
258,5
|
e=625
|
60
from inside
30
from outside
|
0,26
|
adequate
|
47
(-2,-8)
|
29,52
|
39,5
|
|
awrhho02a-06
|
E
F
|
160,0
160,0
|
construction timber
cellulose fibre [0,040; R=55]
|
258,5
|
e=625
|
60
from inside
30
from outside
|
0,26
|
adequate
|
47
(-2,-8)
|
19,30
|
42,7
|
|
awrhho02a-07
|
E
F
|
160,0
160,0
|
construction timber
sheep wool [0,041; R=26]
|
258,5
|
e=625
|
60
from inside
30
from outside
|
0,29
|
adequate
|
47
(-2,-8)
|
19,96
|
37,1
|
|
awrhho02a-08
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
258,5
|
e=400
|
60
from inside
30
from outside
|
0,28
|
adequate
|
47
(-2,-8)
|
24,43
|
41,2
|