Register of building materials used for this application, cross-section
(from outside to inside)
|
Thickness [mm] |
Building material |
Thermal performance |
Reaction to fireklasse EN |
λ |
μ min – max |
ρ |
c |
A |
24,0
|
larch wood
external wall cladding
|
0,155
|
150
|
600
|
1,600
|
D
|
B |
24,0
|
spruce wood
cross battens
|
0,120
|
50
|
450
|
1,600
|
D
|
C |
50,0
|
wood wool composite boards
|
0,090
|
2-5
|
370
|
2,000
|
B
|
D |
15,0
|
fibreboard (MDF)
|
0,140
|
11
|
600
|
1,700
|
D
|
E |
|
construction timber
(60/..; e=*)
|
0,120
|
50
|
450
|
1,600
|
D
|
F |
|
- variable insulation material
|
|
|
|
|
|
G |
15,0
|
OSB
(sealed with airtight tape)
|
0,130
|
200
|
600
|
1,700
|
D
|
H |
15,0
|
gypsum fibre board
or
|
0,320
|
21
|
1000
|
1,100
|
A2
|
H |
15,0
|
gypsum plaster board type DF
|
0,250
|
10
|
800
|
1,050
|
A2
|
Variations of building components
|
Thickness of layer |
Note |
Fire performance |
Thermal performance |
Acoustic performance |
Eco Sustainability |
Mass |
|
Thickness [mm] |
Building material |
Σ |
REI |
U [W/(m²K)] |
Diffusion |
Rw (C,Ctr) [dB] |
ΔOI3 |
m [kg/m²] |
awroho01b-00
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
303,0
|
e=625
|
60
from inside
30
from outside
|
0,21
|
adequate
|
51
(-1,-6)
|
25,66
|
75,8
|
awroho01b-01
|
E
F
|
120,0
120,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
263,0
|
e=625
|
60
from inside
30
from outside
|
0,25
|
adequate
|
50
(-1,-6)
|
23,01
|
3,3
|
awroho01b-02
|
E
F
|
200,0
200,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
343,0
|
e=625
|
60
from inside
30
from outside
|
0,18
|
adequate
|
52
(-1,-6)
|
28,30
|
78,3
|
awroho01b-03
|
E
F
|
240,0
240,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
383,0
|
e=625
|
60
from inside
30
from outside
|
0,16
|
adequate
|
53
(-1,-6)
|
30,95
|
80,8
|
awroho01b-04
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [035; 50; <1000°C]
|
303,0
|
e=625
|
60
from inside
30
from outside
|
0,19
|
adequate
|
52
(-1,-6)
|
43,82
|
80,7
|
awroho01b-05
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [038; ≥33; ≥1000°C]
|
303,0
|
e=625
|
60
from inside
30
from outside
|
0,21
|
adequate
|
51
(-1,-6)
|
30,34
|
78,2
|
awroho01b-06
|
E
F
|
160,0
160,0
|
construction timber
cellulose fibre [040; E]
|
303,0
|
e=625
|
60
from inside
30
from outside
|
0,21
|
adequate
|
51
(-1,-6)
|
20,12
|
81,4
|
awroho01b-07
|
E
F
|
160,0
160,0
|
construction timber
sheep wool [0,041; R=26]
|
303,0
|
e=625
|
60
from inside
30
from outside
|
0,23
|
adequate
|
51
(-1,-6)
|
20,78
|
75,8
|
awroho01b-08
|
E
F
|
160,0
160,0
|
construction timber
mineral wool [040; ≥16; <1000°C]
|
303,0
|
e=400
|
60
from inside
30
from outside
|
0,22
|
adequate
|
51
(-1,-6)
|
25,25
|
79,9
|
Last update 02.08.2023/hfa.eco2soft