Regional validity

Scope

timber frame construction
Cross-section of standard configuration

timber frame construction
Standard configuration

Register of building materials used for this application, cross-section (from outside to inside)

Thickness [mm] Building material Thermal performance Reaction to fire­
λ μ min – max ρ c
A 4,0 plaster 1,000 10-35 2000 1,130 A1
B - variable building material
C 15,0 fibreboard (MDF) 0,140 11 600 1,700 D
D construction timber (60/..; e=*) 0,120 50 450 1,600 D
E - variable insulation material
F 15,0 OSB 0,130 200 600 1,700 D
G vapour barrier sd≥ 9m 1000
H spruce wood cross battens (a=400) or battens offset) 0,120 50 450 1,600 D
I - variable insulation material or air layer in type 02
J 12,5 gypsum plaster board type DF or 0,250 10 800 1,050 A2
J 12,5 gypsum fibre board 0,320 21 1000 1,100 A2

Variations of building components

Thickness of layer Note Fire performance Thermal performance Acoustic performance Eco Sustainability Mass
Thickness [mm] Building material Σ REI U [W/(m²K)] Diffusion Rw (C,Ctr) OI3Kon m [kg/m²]
awropi07a-00 B
D
E
H
I
50,0
160,0
160,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
296,5 e=625 60 from inside
30 from outside
0,17 adequate 45 (-3,-6) 13,65 49,7
awropi07a-01 B
D
E
H
I
50,0
120,0
120,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
256,5 e=625 60 from inside
30 from outside
0,19 adequate 44 (-3,-6) 11,13 47,2
awropi07a-02 B
D
E
H
I
50,0
160,0
160,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
296,5 e=625 ; I=without insulation 60 from inside
30 from outside
0,19 adequate 45 (-3,-6) 11,39 49,2
awropi07a-03 B
D
E
H
I
50,0
200,0
200,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
336,5 e=625 60 from inside
30 from outside
0,15 adequate 46 (-3,-6) 16,18 52,2
awropi07a-04 B
D
E
H
I
50,0
240,0
240,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
376,5 e=625 60 from inside
30 from outside
0,13 adequate 48 (-3,-6) 18,70 54,7
awropi07a-05 B
D
E
H
I
50,0
200,0
200,0
80,0
80,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
376,5 e=625 60 from inside
30 from outside
0,13 adequate 46 (-3,-6) 18,42 55,3
awropi07a-06 B
D
E
H
I
50,0
240,0
240,0
80,0
80,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
416,5 e=625 60 from inside
30 from outside
0,12 adequate 48 (-3,-6) 20,94 57,8
awropi07a-07 B
D
E
H
I
50,0
160,0
160,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [035; 50; <1000°C]
spruce wood
mineral wool [035; 50; <1000°C]
296,5 e=625 60 from inside
30 from outside
0,15 adequate 46 (-3,-6) 38,98 55,8
awropi07a-08 B
D
E
H
I
50,0
160,0
160,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [038; ≥33; ≥1000°C]
spruce wood
mineral wool [038; ≥33; ≥1000°C]
296,5 e=625 60 from inside
30 from outside
0,17 adequate 45 (-3,-6) 16,18 52,8
awropi07a-09 B
D
E
H
I
50,0
160,0
160,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
cellulose fibre [040; E]
spruce wood
cellulose fibre [040; E]
296,5 e=625 60 from inside
30 from outside
0,17 adequate 45 (-3,-6) 7,02 56,7
awropi07a-10 B
D
E
H
I
50,0
160,0
160,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
sheep wool [0,041; R=26]
spruce wood
sheep wool [0,041; R=26]
296,5 e=625 60 from inside
30 from outside
0,18 adequate 45 (-3,-6) 5,69 49,7
awropi07a-11 B
D
E
H
I
50,0
160,0
160,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
296,5 e=400 60 from inside
30 from outside
0,17 adequate 45 (-3,-6) 13,32 53,8
awropi07a-12 B
D
E
H
I
160,0
160,0
160,0
40,0
40,0
Polystyrene EPS-F [0,040]
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
411,5 e=625 60 from inside
30 from outside
0,11 adequate 45 (-3,-6) 26,65 51,6
awropi07a-13 B
D
E
H
I
50,0
160,0
160,0
40,0
40,0
Elasticized polystyrene FS
construction timber
mineral wool [040; ≥16; <1000°C]
spruce wood
mineral wool [040; ≥16; <1000°C]
296,5 e=625 60 from inside
30 from outside
0,17 adequate 47 (-3,-6) 13,65 49,7

Last update 30.08.2017/hfa.plb